Liz@lzsco.com Copy
In different standard, 316 stainless steel has different specification, stainless steel 316 equals as X5CrNiMo17-12-2, SUS316, 1.4401, 03X18H10 etc. The details as the following chart:
| 1.4401 | 316 | X5CrNiMo17-12-2 | SUS316 | Z6CND17-11 | X5CrNiMo17-12-2 | S31600 | 0Cr17Ni12Mo2 | 08KH16N11M3 |
|
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
N |
Mo |
|
Min |
– |
– |
– |
– |
– |
16 |
10 |
– |
2 |
|
Max |
0.08 |
0.75 |
2 |
0.045 |
0.03 |
18 |
14 |
0.1 |
3 |
| Grade | 316 Bar and Section (up to 160 mm thick) | 316 Sheet (up to 8 mm thick) | 316 Plate (8 – 75 mm thick) | 316L Bar and Section (up to 160 mm) | 316L Sheet (up to 8 mm thick) | 316 L Plate (8 – 75 mm thick) | 316H Bar (up to 160 mm) | 316Ti Bar (up to 160 mm) |
| Tensile Strength (MPa) | 500 – 700 | 530 – 680 | 520 – 670 | 500 – 700 | 530 – 680 | 520 – 670 | 490 – 690 | 500 – 700 |
| Proof Stress (MPa) | 200 Min | 240 Min | 220 Min | 200 Min | 240 Min | 220 Min | 205 Min | 200 Min |
| Elongation A50 mm | 40 Min % | 40 Min % | 45 Min % | 40 Min % | 40 Min % | 45 Min % | 35% | 40 Min % |
| Hardness Brinell | 215 Max HB | – | – | 215 Max HB | – | – | – | 215 Max HB |
| Property | Density | Melting Point | Modulus of Elasticity | Electrical Resistivity | Thermal Conductivity | Thermal Expansion |
| Value | 8.00 g/cm3 | 1400°C | 193 GPa | 0.74 x 10-6 Ω.m | 16.3 W/m.K | 15.9 x 10-6/K |
Grade 316, because of the addition of Mo, corrosion resistance, atmospheric corrosion resistance and high-temperature strength is particularly good, can be used in harsh conditions, excellent work hardening, non-magnetic.
A.Construction encasement
B.Off-shore technology
C.Food industry
D.Coastal facilities
E.Equipment for use in seawater
F.Pipe fittings
G.Etc